CORE-BRIGHT 316L

ESAB

CORE-BRIGHT 316L

The following items have been added to your list


x

Welds types 316, 316L and 318 steels. Contain 2-2.5% molybdenum to increase the corrosion resistance to pitting induced by sulfuric and sulfurous acids, sulphites, chloride, and cellulose solutions. Used extensively in the rayon, dye, and paper industries.

BUY NOW


Typical Weld Metal Analysis %

Approvals

Society CERTIFIED BY C.W.B.- AWS A5.22
Society ASME SFA 5.22
Grade E316LTO-3
Society AWS A5.22

Classifications

Grade E316LT0-3
Name AWS A5.22

Typical Tensile Properties

ConditionElongationTensile Strength Yield Strength
As Welded42 %87 ksi (600 MPa)62 ksi (430 MPa)

Deposition Data

Current 110 A
Deposition Rate 5.8 lb/h (2.6 kg/h)
Deposition Type 5
Diameter .045 in. (1.2 mm)
Efficiency (%) 86 %
TTW Dist. 3/4 in. (19 mm)
Voltage 26 V
Wire Feed Speed 300 in./min (762 cm/min)
Current 150 A
Deposition Rate 8.1 lb/h (3.67 kg/h)
Deposition Type 5
Diameter .045 in. (1.2 mm)
Efficiency (%) 86 %
TTW Dist. 3/4 in. (19 mm)
Voltage 27 V
Wire Feed Speed 400 in./min (1016 cm/min)
Current 180 A
Deposition Rate 9.8 lb/h (4.45 kg/h)
Deposition Type 5
Diameter .045 in. (1.2 mm)
Efficiency (%) 87 %
TTW Dist. 3/4 in. (19 mm)
Voltage 27 V
Wire Feed Speed 500 in./min (1270 cm/min)
Current 250 A
Deposition Rate 8.4 lb/h (3.8 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 85 %
TTW Dist. 1 in. (25.4 mm)
Voltage 26 V
Wire Feed Speed 112 in./min (284 cm/min)
Current 250 A
Deposition Rate 10.0 lb/h (4.5 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 89 %
TTW Dist. 1-1/2 in. (38 mm)
Voltage 26 V
Wire Feed Speed 133 in./min (338 cm/min)
Current 300 A
Deposition Rate 10.2 lb/h (4.6 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 85 %
TTW Dist. 1 in. (25.4 mm)
Voltage 28 V
Wire Feed Speed 136 in./min (345 cm/min)
Current 300 A
Deposition Rate 13.5 lb/h (6.1 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 89 %
TTW Dist. 1-1/2 in. (38 mm)
Voltage 28 V
Wire Feed Speed 178 in./min (402 cm/min)
Current 350 A
Deposition Rate 13.9 lb/h (6.3 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 88 %
TTW Dist. 1 in. (25.4 mm)
Voltage 29 V
Wire Feed Speed 184 in./min (467 cm/min)
Current 350 A
Deposition Rate 17.1 lb/h (7.8 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 87 %
TTW Dist. 1-1/2 in. (38 mm)
Voltage 29 V
Wire Feed Speed 227 in./min (577 cm/min)
Current 400 A
Deposition Rate 16.2 lb/h (7.3 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 85 %
TTW Dist. 1 in. (25.4 mm)
Voltage 30 V
Wire Feed Speed 221 in./min (561 cm/min)
Current 400 A
Deposition Rate 22.7 lb/h (10.3 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 87 %
TTW Dist. 1-1/2 in. (38 mm)
Voltage 30 V
Wire Feed Speed 302 in./min (767 cm/min)
Current 450 A
Deposition Rate 20.6 lb/h (9.3 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 85 %
TTW Dist. 1 in. (25.4 mm)
Voltage 30 V
Wire Feed Speed 273 in./min (693 cm/min)
Current 450 A
Deposition Rate 25.9 lb/h (11.7 kg/h)
Deposition Type 5
Diameter 3/32 in. (2.4 mm)
Efficiency (%) 87 %
TTW Dist. 1-1/2 in. (38 mm)
Voltage 30 V
Wire Feed Speed 343 in./min (871 cm/min)
Current 210 A
Deposition Rate 7.1 lb/h (3.2 kg/h)
Deposition Type 5
Diameter 5/64 in. (2.0 mm)
Efficiency (%) 86 %
TTW Dist. 3/4 in. (19 mm)
Voltage 24 V
Wire Feed Speed 137 in./min (348 cm/min)
Current 250 A
Deposition Rate 9.5 lb/h (4.3 kg/h)
Deposition Type 5
Diameter 5/64 in. (2.0 mm)
Efficiency (%) 87 %
TTW Dist. 3/4 in. (19 mm)
Voltage 26 V
Wire Feed Speed 181 in./min (460 cm/min)
Current 300 A
Deposition Rate 12.0 lb/h (5.4 kg/h)
Deposition Type 5
Diameter 5/64 in. (2.0 mm)
Efficiency (%) 85 %
TTW Dist. 3/4 in. (19 mm)
Voltage 27 V
Wire Feed Speed 236 in./min (599 cm/min)
x

Part Numbers and Accessories

Part Numbers : CORE-BRIGHT 316L
CB 316L 3/32X50#CL 251933305 FIND A DISTRIBUTOR