Coreweld C6
Coreweld C6 was developed and "fine-tuned" especially for hand-held, automatic and robotic welding in the automotive industry, as well as rail car manufacturing, structural welding and other similar applications. Never before has there been such a perfect pairing of filler metal and industry requirements for quality, productivity and profitability.
Industries
- Automotive
- Bridge Construction
- Civil Construction
- Industrial and General Fabrication
- Mobile Equipment
- Railcars
- Ship/Barge Building
Welding Process
- MCAW - Metal Core Arc Welding
Typical Weld Metal Analysis %
| Weld Metal Analysis | ||||||||||
| Element | P | C | Mn | C | S | Si | S | P | Si | Mn |
| Nominal Percentage | 0.012 % | 0.04 % | 1.6 % | 0.04 % | 0.016 % | 0.7 % | 0.017 % | 0.015 % | 0.8 % | 1.6 % |
| Shielding Gas | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 90% Ar - 10% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 90% Ar - 10% CO2 | 90% Ar - 10% CO2 | 90% Ar - 10% CO2 | 90% Ar - 10% CO2 |
Approvals
| Society | ABS |
| Grade | CSA W48 E491C-6M-H4 |
| Society | CWB |
Typical Charpy V-Notch Properties
| Condition | 1 |
| Shielding Gas | 75% Ar - 25% CO2 |
| Testing Temperature | -20 degF (-29 degC) |
| Condition | 1 |
| Shielding Gas | 90% Ar - 10% CO2 |
| Testing Temperature | -20 degF (-29 degC) |
| Condition | 1 |
| Shielding Gas | 75% Ar - 25% CO2 |
| Testing Temperature | -40 degF (-40 degC) |
Classifications
| Grade | E70T15-M20A2-CS1-H4 |
| Name | AWS A5.36 |
| Grade | E70T15-M21A4-CS1-H4 |
| Name | AWS A5.36 |
| Grade | E70C-6MD H4 |
| Name | AWS A5.18 |
| Name | ASME SFA 5.36 |
| Name | ASME SFA 5.18 |
Typical Tensile Properties
| Condition | As Welded | As Welded |
| Reduction in Area | 63 % | 64 % |
| Shielding Gas | 90% Ar - 10% CO2 | 75% Ar - 25% CO2 |
| Tensile Strength (imp) | 86 ksi | 86 ksi |
| Tensile Strength (met) | 595 MPa | 595 MPa |
| Yield Strength (imp) | 79 ksi | 74 ksi |
| Yield Strength (met) | 545 MPa | 505 MPa |
| Elongation | 25 % | 27 % |
Deposition Data
| Current | 430-510 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 30-33 V |
| Wire Feed Speed | 350-480 in./min (889-1219 cm/min) |
| Current | 370-430 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 28-30 V |
| Wire Feed Speed | 280-350 in./min (711-889 cm/min) |
| Current | 230-370 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 24-28 V |
| Wire Feed Speed | 150-280 in./min (381-711 cm/min) |
| Current | 370-420 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 30-32 V |
| Wire Feed Speed | 450-550 in./min (1143-1397 cm/min) |
| Current | 310-370 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 27-30 V |
| Wire Feed Speed | 350-450 in./min (889-1143 cm/min) |
| Current | 190-310 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 24-27 V |
| Wire Feed Speed | 180-350 in./min (457-889 cm/min) |
| Current | 330-390 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 29-32 V |
| Wire Feed Speed | 500-650 in./min (1270-1651 cm/min) |
| Current | 260-330 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 26-29 V |
| Wire Feed Speed | 350-500 in./min (889-1270 cm/min) |
| Current | 170-260 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 24-26 V |
| Wire Feed Speed | 200-350 in./min (508-889 cm/min) |
| Current | 340-430 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 29-32 V |
| Wire Feed Speed | 250-350 in./min (635-889 cm/min) |
| Current | 230-340 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 26-29 V |
| Wire Feed Speed | 150-250 in./min (381-635 cm/min) |
| Current | 340-410 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 31-36 V |
| Wire Feed Speed | 400-530 in./min (1016-1346 cm/min) |
| Current | 280-340 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 28-31 V |
| Wire Feed Speed | 300-400 in./min (762-1016 cm/min) |
| Current | 190-280 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 29-28 V |
| Wire Feed Speed | 180-300 in./min (457-762 cm/min) |
| Current | 200-260 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 27-28 V |
| Wire Feed Speed | 250-350 in./min (635-889 cm/min) |
| Current | 260-310 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 28-30 V |
| Wire Feed Speed | 350-450 in./min (889-1143 cm/min) |
| Current | 200 A |
| Deposition Rate | 6.5 lb/h (3.0 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 95 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 27 V |
| Wire Feed Speed | 250 in./min (640 cm/min) |
| Current | 260 A |
| Deposition Rate | 9.1 lb/h (4.1 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 97 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 28 V |
| Wire Feed Speed | 350 in./min (890 cm/min) |
| Current | 290 A |
| Deposition Rate | 10.2 lb/h (4.6 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 98 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 29 V |
| Wire Feed Speed | 400 in./min (1020 cm/min) |
| Current | 330 A |
| Deposition Rate | 12.7 lb/h (5.8 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 32 V |
| Wire Feed Speed | 500 in./min (1270 cm/min) |
| Current | 190 A |
| Deposition Rate | 5.5 lb/h (2.5 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 94 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 26 V |
| Wire Feed Speed | 180 in./min (440 cm/min) |
| Current | 240 A |
| Deposition Rate | 7.7 lb/h (3.5 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 95 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 27 V |
| Wire Feed Speed | 250 in./min (640 cm/min) |
| Current | 280 A |
| Deposition Rate | 9.2 lb/h (4.2 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 97 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 28 V |
| Wire Feed Speed | 300 in./min (760 cm/min) |
| Current | 340 A |
| Deposition Rate | 11.2 lb/h (5.1 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 31 V |
| Wire Feed Speed | 400 in./min (1020 cm/min) |
| Current | 410 A |
| Deposition Rate | 15.7 lb/h (7.1 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 36 V |
| Wire Feed Speed | 530 in./min (1330 cm/min) |
| Current | 230 A |
| Deposition Rate | 6.2 lb/h (2.81 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 91 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 26 V |
| Wire Feed Speed | 150 in./min (380 cm/min) |
| Current | 290 A |
| Deposition Rate | 8.8 lb/h (4.0 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 95 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 27 V |
| Wire Feed Speed | 200 in./min (510 cm/min) |
| Current | 340 A |
| Deposition Rate | 12.3 lb/h (5.6 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 98 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 29 V |
| Wire Feed Speed | 250 in./min (640 cm/min) |
| Current | 510 A |
| Deposition Rate | 20.7 lb/h (9.4 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 36 V |
| Wire Feed Speed | 480 in./min (1210 cm/min) |
| Current | 430-510 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 32-36 V |
| Wire Feed Speed | 350-480 in./min (889-1219 cm/min) |
| Current | 310-360 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 30-33 V |
| Wire Feed Speed | 450-550 in./min (1143-1397 cm/min) |
| Current | 170 A |
| Deposition Rate | 5.2 lb/h (2.4 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 94 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 24 V |
| Wire Feed Speed | 200 in./min (510 cm/min) |
| Current | 230 A |
| Deposition Rate | 7.7 lb/h (3.5 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 96 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 25 V |
| Wire Feed Speed | 300 in./min (760 cm/min) |
| Current | 290 A |
| Deposition Rate | 10.2 lb/h (4.6 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 98 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 27 V |
| Wire Feed Speed | 400 in./min (1020 cm/min) |
| Current | 330 A |
| Deposition Rate | 12.7 lb/h (5.8 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 32 V |
| Wire Feed Speed | 500 in./min (1270 mm/min) |
| Current | 330 A |
| Deposition Rate | 12.7 lb/h (5.8 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 29 V |
| Wire Feed Speed | 500 in./min (1270 cm/min) |
| Current | 360 A |
| Deposition Rate | 13.9 lb/h (6.3 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 33 V |
| Wire Feed Speed | 550 in./min (1400 cm/min) |
| Current | 390 A |
| Deposition Rate | 16.5 lb/h (7.5 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 32 V |
| Wire Feed Speed | 650 in./min (1650 cm/min) |
| Current | 190 A |
| Deposition Rate | 5.5 lb/h (2.5 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 94 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 24 V |
| Wire Feed Speed | 180 in./min (440 cm/min) |
| Current | 240 A |
| Deposition Rate | 7.7 lb/h (3.5 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 95 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 25 V |
| Wire Feed Speed | 250 in./min (640 cm/min) |
| Current | 310 A |
| Deposition Rate | 10.7 lb/h (4.9 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 98 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 27 V |
| Wire Feed Speed | 350 in./min (890 cm/min) |
| Current | 370 A |
| Deposition Rate | 13.6 lb/h (6.2 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 30 V |
| Wire Feed Speed | 450 in./min (1140 cm/min) |
| Current | 420 A |
| Deposition Rate | 16.6 lb/h (7.5 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8 in. (16 mm) |
| Voltage | 32 V |
| Wire Feed Speed | 550 in./min (1400 cm/min) |
| Current | 230 A |
| Deposition Rate | 6.2 lb/h (2.81 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 91 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 24 V |
| Wire Feed Speed | 150 in./min (380 cm/min) |
| Current | 290 A |
| Deposition Rate | 8.8 lb/h (4.0 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 95 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 26 V |
| Wire Feed Speed | 200 in./min (510 cm/min) |
| Current | 370 A |
| Deposition Rate | 12.5 lb/h (5.7 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 96 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 28 V |
| Wire Feed Speed | 280 in./min (700 cm/min) |
| Current | 430 A |
| Deposition Rate | 15.9 lb/h (7.2 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 29 V |
| Wire Feed Speed | 350 in./min (890 cm/min) |
| Current | 430 A |
| Deposition Rate | 15.9 lb/h (7.2 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 90% Ar - 10% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 32 V |
| Wire Feed Speed | 350 in./min (890 cm/min) |
| Current | 510 A |
| Deposition Rate | 20.7 lb/h (9.4 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 99 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4 in. (19 mm) |
| Voltage | 33 V |
| Wire Feed Speed | 480 in./min (1210 cm/min) |