Dual Shield 710X
Dual Shield 710X is an all-position flux cored wire for general purpose welding. It provides outstanding operator appeal with an easily controlled arc, improved operation at both lower and higher current levels, minimal spatter and easily removed slag. Dual Shield 710X can be used with 100% CO2, recommended in applications where weld joint restraint is high. Applications include rail car, barges, civil construction, light equipment and general fabrication.
Industries
- Barges
- Civil Construction
- Industrial and General Fabrication
- Railcars
- Ship/Barge Building
- Light Equipment
Welding Process
- FCAW (Flux Core)
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||
| Element | Ni | S | P | Si | Mn | C | Ni | S | P | Si | Mn | C |
| Nominal Percentage | 0.4 % | 0.009 % | 0.007 % | 0.5 % | 1.4 % | 0.03 % | 0.4 % | 0.009 % | 0.005 % | 0.6 % | 1.5 % | 0.03 % |
| Shielding Gas | 100% CO2 | 100% CO2 | 100% CO2 | 100% CO2 | 100% CO2 | 100% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 |
Approvals
| Society | ABS |
| Society | LR |
| Society | DNV-GL |
| Grade | CSA W48 E491T-9-H8 |
| Society | CWB |
| Society | Seismic Certified “D” |
Typical Charpy V-Notch Properties
| Condition | 1 |
| Shielding Gas | 75% Ar - 25% CO2 |
| Testing Temperature | 0 degF (-18 degC) |
| Condition | 1 |
| Shielding Gas | 75% Ar - 25% CO2 |
| Testing Temperature | -20 degF (-29 degC) |
| Condition | 1 |
| Shielding Gas | 100% CO2 |
| Testing Temperature | 0 degF (-18 degC) |
| Condition | 1 |
| Shielding Gas | 100% CO2 |
| Testing Temperature | -20 degF (-29 degC) |
Classifications
| Name | ASME SFA 5.36 |
| Name | ASME SFA 5.20 |
| Grade | E71T1-C1A2-CS1-DH8 |
| Name | AWS A5.36 |
| Grade | E71T-1C-DH8/T-9C-DH8 |
| Name | AWS A5.20 |
Typical Tensile Properties
| Condition | As Welded | As Welded |
| Shielding Gas | 75% Ar - 25% CO2 | 100% CO2 |
| Tensile Strength (imp) | 93 ksi | 87 ksi |
| Tensile Strength (met) | 640 MPa | 625 MPa |
| Yield Strength (imp) | 83 ksi | 75 ksi |
| Yield Strength (met) | 570 MPa | 520 MPa |
| Elongation | 27 % | 28 % |
Deposition Data
| Current | 135-205 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 3/8-1/2 in. (9.5-12.7 mm) |
| Voltage | 23-26 V |
| Wire Feed Speed | 170-290 in./min (432-737 cm/min) |
| Current | 180-265 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 3/4-1 in. (19-25.4 mm) |
| Voltage | 26-30 V |
| Wire Feed Speed | 350-550 in./min (889-1397 cm/min) |
| Current | 250-350 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 3/4-1 in. (19-25.4 mm) |
| Voltage | 29-31 V |
| Wire Feed Speed | 400-600 in./min (1016-1524 cm/min) |
| Current | 245-345 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 3/4-1 in. (19-25.4 mm) |
| Voltage | 27-30 V |
| Wire Feed Speed | 265-400 in./min (673-1016 cm/min) |
| Current | 290-415 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 1-1.25 in. (25.4-31.75 mm) |
| Voltage | 28-32 V |
| Wire Feed Speed | 400-500 in./min (1016-1270 cm/min) |
| Current | 250-340 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4-1 in. (19-25.4 mm) |
| Voltage | 27-30 V |
| Wire Feed Speed | 240-320 in./min (610-813 cm/min) |
| Current | 185-265 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4-1 in. (19-25.4 mm) |
| Voltage | 27-29 V |
| Wire Feed Speed | 305-470 in./min (775-1194 cm/min) |
| Current | 130-200 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/8-1/2 in. (9.5-12.7 mm) |
| Voltage | 22-26 V |
| Wire Feed Speed | 140-240 in./min (356-610 cm/min) |
| Current | 285-400 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 1-1.25 in. (25.4-31.75 mm) |
| Voltage | 28-32 V |
| Wire Feed Speed | 320-460 in./min (813-1168 cm/min) |
| Current | 185-285 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8-3/4 in. (15.8-19 mm) |
| Voltage | 24-28 V |
| Wire Feed Speed | 140-240 in./min (356-610 cm/min) |
| Current | 225-295 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 5/8-3/4 in. (15.8-19 mm) |
| Voltage | 27-30 V |
| Wire Feed Speed | 270-370 in./min (686-940 cm/min) |
| Current | 135-250 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 1/2-5/8 in. (12.7-15.8 mm) |
| Voltage | 24-28 V |
| Wire Feed Speed | 125-270 in./min (317.5-686 cm/min) |
| Current | 165-270 A |
| Deposition Type | 3 |
| Diameter | 1/16 in. (1.6 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 5/8-3/4 in. (15.8-19 mm) |
| Voltage | 25-28 V |
| Wire Feed Speed | 135-265 in./min (343-673 cm/min) |
| Current | 215-290 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 5/8-3/4 in. (15.8-19 mm) |
| Voltage | 25-29 V |
| Wire Feed Speed | 280-400 in./min (711-1016 cm/min) |
| Current | 125-235 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 1/2-5/8 in. (12.7-15.8 mm) |
| Voltage | 23-26 V |
| Wire Feed Speed | 130-280 in./min (330-711 cm/min) |
| Current | 175-230 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 100% CO2 |
| TTW Dist. | 1/2-3/4 in. (12.7-19 mm) |
| Voltage | 25-27 V |
| Wire Feed Speed | 290-350 in./min (737-889 cm/min) |
| Current | 140 A |
| Deposition Rate | 3.3 lb/h (1.5 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 23 V |
| Wire Feed Speed | 190 in./min (483 cm/min) |
| Current | 184 A |
| Deposition Rate | 5.3 lb/h (2.4 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 210 in./min (533 cm/min) |
| Current | 190 A |
| Deposition Rate | 5.5 lb/h (2.5 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 220 in./min (559 cm/min) |
| Current | 187 A |
| Deposition Rate | 4.2 lb/h (1.9 kg/h) |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 80 % |
| Shielding Gas | 100% CO2 |
| Voltage | 24 V |
| Wire Feed Speed | 140 in./min (356 cm/min) |
| Current | 245-355 A |
| Deposition Type | 3 |
| Diameter | .052 in. (1.4 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 3/4-1 in. (19-25.4 mm) |
| Voltage | 245-355 V |
| Wire Feed Speed | 370-540 in./min (940-1372 cm/min) |
| Current | 165-225 A |
| Deposition Type | 3 |
| Diameter | .045 in. (1.2 mm) |
| Shielding Gas | 75% Ar - 25% CO2 |
| TTW Dist. | 1/2-3/4 in. (12.7-19 mm) |
| Voltage | 24-27 V |
| Wire Feed Speed | 610-775 in./min (240-305 cm/min) |
| Current | 154 A |
| Deposition Rate | 3.9 lb/h (1.77 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 23 V |
| Wire Feed Speed | 220 in./min (559 cm/min) |
| Current | 167 A |
| Deposition Rate | 4.5 lb/h (2.04 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 82 % |
| Shielding Gas | 100% CO2 |
| Voltage | 24 V |
| Wire Feed Speed | 250 in./min (635 cm/min) |
| Current | 180 A |
| Deposition Rate | 5.1 lb/h (2.31 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 82 % |
| Shielding Gas | 100% CO2 |
| Voltage | 24 V |
| Wire Feed Speed | 280 in./min (711 cm/min) |
| Current | 193 A |
| Deposition Rate | 5.6 lb/h (2.54 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 82 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 310 in./min (787 cm/min) |
| Current | 205 A |
| Deposition Rate | 6.2 lb/h (2.81 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 83 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 340 in./min (864 cm/min) |
| Current | 217 A |
| Deposition Rate | 6.8 lb/h (3.08 kg/h) |
| Deposition Type | 6 |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 83 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 370 in./min (940 cm/min) |
| Current | 153 A |
| Deposition Rate | 4.0 lb/h (1.81 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 24 V |
| Wire Feed Speed | 160 in./min (406 cm/min) |
| Current | 159 A |
| Deposition Rate | 4.0 lb/h (1.81 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 24 V |
| Wire Feed Speed | 170 in./min (432 cm/min) |
| Current | 166 A |
| Deposition Rate | 4.5 lb/h (2.04 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 180 in./min (457 cm/min) |
| Current | 172 A |
| Deposition Rate | 4.8 lb/h (2.17 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 190 in./min (483 cm/min) |
| Current | 178 A |
| Deposition Rate | 5.0 lb/h (2.27 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 200 in./min (508 cm/min) |
| Current | 196 A |
| Deposition Rate | 5.8 lb/h (2.63 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 82 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 230 in./min (584 cm/min) |
| Current | 201 A |
| Deposition Rate | 6.0 lb/h (2.72 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 82 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 240 in./min (610 cm/min) |
| Current | 207 A |
| Deposition Rate | 6.3 lb/h (2.86 kg/h) |
| Deposition Type | 6 |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 82 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 250 in./min (635 cm/min) |
| Current | 205 A |
| Deposition Rate | 4.9 lb/h (2.22 kg/h) |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 80 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 160 in./min (406 cm/min) |
| Current | 223 A |
| Deposition Rate | 5.6 lb/h (2.54 kg/h) |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 80 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 180 in./min (457 cm/min) |
| Current | 240 A |
| Deposition Rate | 6.3 lb/h (2.86 kg/h) |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 80 % |
| Shielding Gas | 100% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 200 in./min (508 cm/min) |
| Current | 257 A |
| Deposition Rate | 7.0 lb/hr lb/h |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 220 in./min (559 cm/min) |
| Current | 273 A |
| Deposition Rate | 7.7 lb/hr lb/h |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 240 in./min (610 cm/min) |
| Current | 289 A |
| Deposition Rate | 8.4 lb/hr lb/h |
| Deposition Type | 6 |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 81 % |
| Shielding Gas | 100% CO2 |
| Voltage | 26 V |
| Wire Feed Speed | 260 ipm in./min |