Dual Shield 9000-C1
Dual Shield 9000-C1 is an all-position flux cored electrode which produces a 2.5% Ni deposit. The analysis is very similar to the Dual Shield T-90C1 except that this product has out-of-position capability. Dual Shield 9000-C1 is used for welding of 2-3% Ni steels and castings used in applications requiring good toughness at subzero temperatures. Shielding gas 100% CO2 and 75% Ar - Remainder CO2 may be used.
Industries
- Process
- Ship and Offshore Yards
Welding Process
- FCAW (Flux Core)
Typical Weld Metal Analysis %
| Weld Metal Analysis | ||||||||||||
| Element | S | S | C | C | Si | Si | P | P | Mn | Ni | Mn | Ni |
| Nominal Percentage | 0.010 % | 0.011 % | 0.07 % | 0.08 % | 0.50 % | 0.70 % | 0.014 % | 0.013 % | 1.50 % | 2.60 % | 1.20 % | 2.50 % |
| Shielding Gas | 100% CO2 | 75% Ar - 25% CO2 | 100% CO2 | 75% Ar - 25% CO2 | 100% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 100% CO2 | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 | 100% CO2 | 100% CO2 |
Typical Charpy V-Notch Properties
| Condition | 1 |
| Shielding Gas | 100% CO2 |
| Testing Temperature | 0 degF (-18 degC) |
| Condition | 1 |
| Shielding Gas | 100% CO2 |
| Testing Temperature | -40 degF (-40 degC) |
| Condition | 1 |
| Shielding Gas | 75% Ar - 25% CO2 |
| Testing Temperature | -40 degF (-40 degC) |
Classifications
| Name | ASME SFA 5.29 |
| Name | ASME SFA 5.36 |
| Grade | E91T1-M21A4-Ni2 |
| Name | AWS A5.36 |
| Grade | E91T1-C1A4-Ni2 |
| Name | AWS A5.36 |
| Grade | E91T1-Ni2C/E91T1-Ni2M |
| Name | AWS A5.29 |
Typical Tensile Properties
| Condition | As Welded | As Welded |
| Shielding Gas | 75% Ar - 25% CO2 | 100% CO2 |
| Tensile Strength (imp) | 98 ksi | 96 ksi |
| Tensile Strength (met) | 680 MPa | 665 MPa |
| Yield Strength (imp) | 89 ksi | 85 ksi |
| Yield Strength (met) | 610 MPa | 580 MPa |
| Elongation | 24 % | 25 % |
Deposition Data
| Current | 150 A |
| Deposition Rate | 4.2 lb/h (1.91 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 86 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 28 V |
| Wire Feed Speed | 200 in./min (508 cm/min) |
| Current | 210 A |
| Deposition Rate | 6.3 lb/h (86 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 86 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 29 V |
| Wire Feed Speed | 300 in./min (762 cm/min) |
| Current | 250 A |
| Deposition Rate | 8.5 lb/h (3.86 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 30 V |
| Wire Feed Speed | 400 in./min (1016 cm/min) |
| Current | 290 A |
| Deposition Rate | 10.7 lb/h (4.85 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 33 V |
| Wire Feed Speed | 500 in./min (1270 cm/min) |
| Current | 330 A |
| Deposition Rate | 12.7 lb/h (5.76 kg/h) |
| Diameter | .045 in. (1.2 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 34 V |
| Wire Feed Speed | 600 in./min (1524 cm/min) |
| Current | 155 A |
| Deposition Rate | 4.4 lb/h (2 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 25 V |
| Wire Feed Speed | 150 in./min (381 cm/min) |
| Current | 245 A |
| Deposition Rate | 7.3 lb/h (3.31 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 86 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 28 V |
| Wire Feed Speed | 250 in./min (635 cm/min) |
| Current | 310 A |
| Deposition Rate | 10.2 lb/h (4.63 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 85 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 33 V |
| Wire Feed Speed | 350 in./min (889 cm/min) |
| Current | 360 A |
| Deposition Rate | 13.3 lb/h (6.03 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 85 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 36 V |
| Wire Feed Speed | 450 in./min (1143 cm/min) |
| Current | 430 A |
| Deposition Rate | 17.6 lb/h (7.98 kg/h) |
| Diameter | .052 in. (1.4 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 37 V |
| Wire Feed Speed | 600 in./min (1524 cm/min) |
| Current | 190 A |
| Deposition Rate | 6.1 lb/h (2.77 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 27 V |
| Wire Feed Speed | 150 in./min (38 cm/min) |
| Current | 300 A |
| Deposition Rate | 10.2 lb/h (4.63 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 30 V |
| Wire Feed Speed | 250 in./min (35 cm/min) |
| Current | 365 A |
| Deposition Rate | 12.3 lb/h (5.58 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 86 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 33 V |
| Wire Feed Speed | 300 in./min (762 cm/min) |
| Current | 410 A |
| Deposition Rate | 14 lb/h (6.35 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 88 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 33 V |
| Wire Feed Speed | 350 in./min (889 cm/min) |
| Current | 450 A |
| Deposition Rate | 16 lb/h (7.3 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 33 V |
| Wire Feed Speed | 400 in./min (1016 cm/min) |
| Current | 500 A |
| Deposition Rate | 20.1 lb/h (9.11 kg/h) |
| Diameter | 1/16 in. (1.6 mm) |
| Efficiency (%) | 87 % |
| Shielding Gas | 75% Ar - 25% CO2 |
| Voltage | 39 V |
| Wire Feed Speed | 500 in./min (1270 cm/min) |